How is pot/work life, demold time, and cure time defined?Updated a month ago

Pot Life or Work Time is the amount of time you have after two components have been mixed together before your chemical reaction starts to occur and your compounds will begin to set. Demold Time is the time you have to wait after it is solid enough to remove from your mold box or piece from your mold. At the demold time, it is solidified enough to handle but has not reached a full homogenous cure or it's full strength. Cure Time is when your materials have reached "full strength and cure".